Polymer latex fortified DEPENDABLE SKIMFLOW RS is a durable easy-to-use self-leveling underlayment for most cured concrete and properly prepared floors. SKIMFLOW RS is designed to level and repair surfaces up to 1" thickness. Surfaces such as concrete, mortars, and ceramic floors can be prepared for the installation of carpet, resilient floors, wood parquet, slate, ceramic, tile, marble, granite, or stone veneer floors.
|
|
|
| SKIMFLOW RS is... |
|
|
PHYSICAL CHARACTERISTICS
|
| *Working Time: 20 minutes |
| *Setting Time: 2-3 hours |
| *Ready for Covering: 3-4 hours |
|
*minimum thickness at 70 ° F (21 ° C)
|
| Compressive Strength: over 5,000 psi. (34 MPa) |
| Flexural Strength: 1460 psi. (10 MPa) |
| Tensile Strength: 740 psi. (5 MPa) |
| Coverage: at minimum flowable thickness (about 1/8") about 1 sq. ft per pound. |
| Minimum Thickness: about 1/8" (3.18 mm) |
| Maximum Thickness: 1" per layer (25.4 mm) |
| Mix Ratio: 55 lb bag to 6-1/2 quarts of liquid (24.75 kg bag to 6.15 liters of liquid) |
| Application Conditions: surface and product must be over 50 ° F (10 ° C) and application must not freeze for 7 days |
| Color: medium gray |
| Admixtures: cool, clean water |
| Primers: Primer SL - coverage is 1 gallon per 250-300 sq. ft |
| |
| PACKAGING |
| 55 lb. bag - Kraft paper, double wall bag |
|
 |
Easily mixable with water. |
|
|
Both pumpable and pourable. |
|
|
Flowable for 15-20 minutes. |
|
|
Quick setting to allow covering in 3-4 hours. |
|
|
Compatible with adhesives, mortars, and epoxies. |
|
|
Usable over cutback adhesive residue. |
|
|
Usable as a light duty wear layer. |
|
|
A 21st century product available today! |
|
| PRIMER SL is a specially formulated acrylic latex that improves the flowability, curing and adhesion of SKIMFLOW RS. While SKIMFLOW RS itself will bond to many concrete surfaces, these characteristics are greatly enhanced by using PRIMER SL.
|
|